Photocatalytic Oxidation of Pollutant Dyes in Polluting water by ZnO nano-material

Abstract

Abstract In this study , ZnO Nanoparticles were fabricated by solid state reaction method at room temperature using zinc acetate and oxalic acid.The formed powder was annealed at 300, 400 and 500 C0 for four hours. The synthesized ZnO Nanopartciles were characterized by different techniques. The FTIR spectral data of the chemical bonding indicated that the prepared samples at 400oC and 500oC were ZnO but the prepared sample at 300oC was not successively synthesized. The obtained data from XRD confirmed that the prepared materials were ZnO Nanoparticles. the crystallite size increased with the annealing temperature from 12.9 to 41.5 nm. .The photocatalytic activity was achieved by the degradation of Methyl orange at concentration of 8.5 mg/L in aqueous solution under UV irradiation.

المستخلص في هذه الدراسة تم تخليق أكسيد الزنك في الحجم النانوي (اقل من 100 نانومتر) بطريقة التفكك الحراري في وجود خلات الزنك وحامض الاكسليكفي درجات حرارة مختلقه (oC400oC,500 وoC300) وتم استخدام عدة تقنيات للتأكد من الناتج . المعلومات المتحصل عليها من جهاز الاشعه تحت الحمراء للروابط والزمر الوظيفية للعينتين اللتين حضرتا عند oC400oC,500 أعطت دليل على ان الناتج أكسيد الزنك لكن في العينه المحضره عند oC300لم ينجح تحضيراكسيد الزنك .النتائج المتحصل عليها من جهاز حيود الاشعه السينيةأكدتأن الناتج أكسيد الزنك في الحجم النانوي ووجد أن حجم أكسيد الزنك يزيد مع زيادة درجه الحرارة من 12.9 الى 41.5 نانوميتر. تم اختبار فعالية أكسيد الزنك النانوي في تكسير صبغة الميثيل البرتقالي في محلول مائي بتركيز 8.5 مل /جرام في وجود الاشعه فوق البنفسجية وكانت الفعالية جيده.