Determination of Free Lime in Sudanese Cement Samples

Abstract

Abstract Cement free lime value generally indicates quality of raw materials, the completeness of the clinkering reaction and thequality of the burning practices hence the quality of the cement. A high free lime clinker usually is due either to in homogeneity and coarseness of cement raw mix or to improper burning and cooling condition in the kiln. Excess free lime results in undesirable effects such as volume expansion, increased setting time or reduced strength, hence it is critical to measure free lime content to ensure the quality of cement. The study was concluded on three simple bought from Khartoum In the study the sample who analyzed for its free lime content. It was found that the content of free lime is 0.756 , 08321 , 0.9296 which satistion the specification. The effect of dissolution Of CaO in ethylene glycol with temperature was shaded and it were found that at 50oC. the extraction was found to 0.756% and at 70oC 0.8321 and at 100oC it was found to be 0.9296%. The effect of time onCaO dissolution was found to be 0.9296% of in 10 minute it who 0.952% and of in 20 minute it was to be 0.98%.

تشير قيمة كمية الجير الحر في التحليل الكيميائي للأسمنت إلى جودة المواد الخام، إكتمال عملية المعالجة الحرارية في فرن الحرق، وجودة عمليات الحرق مما يضمن جودة المنتج النهائي. تعود الزيادة في نسبة الجير الحر في عينات الكلنكر إلى عدم تجانس وعدم نعومة مخلوط المواد الخام أو الحرق الغير جيد أو ظروف التبريد السيئة في الفرن. ويؤدي الفائض من الجير الحر في الأسمنت إلى تمدد حجم الجسم الأسمنتي، زيادة في زمن التصلب وضعف في القوة وبذلك يكون قياس كمية الجير الحر مؤشر للجودة. وقد اجريت الدراسة على ثلاثة عينات من السوق المحلي. في هذه الدراسة تم تحليل العينة لمعرفة محتواها من الجير الحر وقد وجدت نسب الجير الحر 0.756 , 08321 , 0.9296 وهي نسب توافق المواصفات.