Optical Properties of LaWxNi1-xO3 Synthesized Using Solid State Reaction Method

Abstract

Abstract The LaWxNi1-xO3porvskite (where x = 0.0, 0.25, and 0.5), respectively was synthesized using solid state reaction method. The chemical structure and the optical properties were studied in details using Fourier transform infrared spectroscopy (FTIR) and Ultra-Violet visible spectroscopy (UV-Vis). FTIR results confirmed the formation of the characteristics absorption bands around 434, 524, 645, 1120, 1638, and 2930 cm−1. The chemical structure was found to decrease with increasing Ni ions and this may be due to the fact that Ni ions (0.69 Å) is larger than that of the W ions (0.62 Å). The energy band gap was calculated for samples with different ratio and was found to be 4.34, 3.95, and 4.45 eV, for the samples with (x= 0.0, 0.25, and 0.5), respectively.

المستخلص تم تحضير العينات ذات الصيغةLaWxNi1-xO3حيث X=0.0, 0.25 , و0.5 باستخدام طريقة تفاعل المواد الصلبة وركزت الدراسة علي التحضير والخواص الضوئية للعينات . وتم التحقق من الخواص الكيمائية للمركبات بواسطة مطياف الاشعة تحت الحمراء ووجد أن الاطوال الموجية للامتصاص تتمركز حول 434 , 524 ,645 , 1120, 1638, 2930سم-1 ووجد أن الاطوال الموجية تقل مع إضافة أيونات النيكل لأن نصف قطر أيون النيكل (Å 0.69) أكبر من نصف قطر أيون التنجستن(0.62 Å). كما تم حساب فجوات الطاقة للعينات من بيانات المطياف الضوئي للاشعة فوق البنفسجية ووجدت 4.34, 3.95, 4.45. إلكترون فولت للعينات (x = صفر ،0,25 ، 0,5) علي التوالي .