Display fingerprints using steel slag powder and optical laser system

Abstract

ABSTRACT

In this study three sample of iron slag powder prepared by three different rates (sample one 20 g from powder and 2.5 g from NaOH, sample two 30g from powder and 5 g from NaOH and sample three 40 g from powder and 7.5 g from NaOH was taken) and compared by control sample. The UV-Visible spectrophotometer was used to carry out the absorption spectrum and then calculated the optical parameters (absorption coefficient, extinction coefficient ,refractive index and reflection).It was found that the absorption of all sample in the range of uv (252-396) nm and the absorption decrease when the rate of processing increase, the maxim absorption coefficient value equal 99.505 cm-1 for (00g: 00g) sample and minim value was 29.23 cm-1 for sample (20g: 2.5g) and the maximal Reflective Index value equal 1.940 for (00g: 00g) sample and minimal value was 1.3 for (20g: 2.5g) sample (20g: 2.5g).The image appears clearly when the iron slag powder enhanced by increasing NaOH, and also the image that has been taken by a laser optical system was more resolved than by the pololight device.

مستخلص البحث

في هذه الدراسة أخذت ثلاث عينات من مسحوق خبث الحديد بثلاث معدلات (g 20من المسحوق g 2.5من NaOH، العينة الثانية 30g من المسحوق مع g 5من NaOH ،العينة الثالثة g 40 من المسحوق مع 7.5gمن NaOH) وقورنت مع العينة الأصلية . أستخدم جهاز UV-spectrophotometer لإيجاد طيف الامتصاص وحساب المعاملات البصرية (معامل الامتصاص ، معامل التوهين ، معامل الإنكسار ، الانعكاس ) وجد طيف الامتصاص للعينات في المديnm(252-396). وجد أن الامتصاص يقل بزيادة معدل المعالجة للمسحوق ، أقصي قيمة معامل امتصاص هي 99.505cm-1 للعينة ( (00g:00gوأقل قيمة امتصاص هي 29.23cm-1للعينة ( (20g:2.5g وأقصي معامل انعكاس هو1.940 للعينة (00g:00g)وأقل قيمة للمعامل الانعكاس هي 1.3للعينة (20g:2.5g).كما وجد أن الصور تظهر أكثر وضوحا مع زيادة NaOH الذي يحسن من خصائص المسحوق ، وأن الصور المأخوذة بواسطة منظومة الليزر أكثر وضوحا من التي أخذت باستخدام جهاز Pololight.