Structural and optical properties of (Zn0.3Ni1-xCuxFe2O4) Nano Particle Synthesis by co-precipitation method

Abstract

Abstract A series of Zinc-nickel-cooper ferrite with compositional formula (Zn0.3Ni1-xCuxFe2O4) nano-particles were(x=0, 0.2, 0.4, 0.6, 0.8,and1.0) were prepared by co-precipitation method and annealed at 450c° for 12 hours. The X-ray diffraction (XRD) and Fourier transformation Infrared Spectroscopy(FTIR) were used to study the structural properties of the nano-particles,the particle size was evaluated by (XRD), while scanning electron microscopy (SEM) was used to study the surface morphology of the nano-particles. The (XRD) results showed that the compound had spinal ferrite, this also was confirmed by the vibration modes observed by (FTIR). The energy gap of the compounds is deduced from UV-Visible spectroscopy and found to be: (3.308, 3.306, 3.303, 3.299, 3.296 and 3.293 eV.),respectively.

المستخلص تم تحضير الزنك- نيكل - نحاس فرايت النانوي(Zn0.3Ni1-xCuxFe2O4) x=(0, 0.2, 0.4, 0.6, 0.8, 1) بتقنية الترسيب المشترك الكيميائية، وتم تسخين المركب في درجة حرارة ) C°450) لمدة 12ساعة، جهاز حيود الأشعة السينية وجهاز مطيافية الأشعة تحت الحمراء أستخدمت لدراسة الخصائص التركيبية. حجم الحبيبات تم إستنتاجه بإستخدام جهاز(XRD) بينما أستخدم جهاز المجهر الإلكتروني الماسح (SEM) لدراسة سطح العينة. نتائج جهاز حيود الأشعة السينية(XRD) تشير إلى أن المركب عبارة عن سبينل فرايت وهذا يتفق مع أنماط الإهتزاز الملاحظة بإستخدام جهاز مطيافية الأشحة تحت الحمراء(FTIR).تم حساب فجوة الطاقة للمركب بإستخدام جهاز مطيافية الأشعة فوق البنفسجيةUV-VIS)) ووجدت3.308, 3.306, 3.303, 3.299,3.296, 3.293) ) الكترون فولت على التوالي.