Synthesis and characterization of cadmium sulfide doped with strontium thin film by spin coating method

Abstract

Cadmium sulfide doped with Strontium thin film were successfully prepared using co-perception

technique and deposited on glass substrate using spin coating method.

XRD studies reveal that the CdS/Sr thin films have orthorhombic structure and the crystalline

size calculated by Scherer's formula found to be equals 5.78nm.

The FTIR spectra for the samples measured in the range of 400-4000

cm

−

1

exhibit showing the

absorption band around 616cm

-1

,1413cm

-1

,

1663cm

-1

,2337cm

-1

.

The Band gaps energy of the materials were calculated from the UV -V is absorption for the

sample Cd1-xSrxS (x=0.00, 0.1, 0.15, 0.30, 0.35), and they were found to be 1.67eV, 1.79eV,

1.87eV, 2eV, 2.09eV which are semiconductor.

المستخلص

تم تحضير شرائح كبريتيد الكادميوم المشوب بعنصر السترانشيوم باستخدام تقنيه الترسيب المشترك بنجاح

وقد رسب علي شرائح زجاجيه باستخدام طريقه الطلء المغزلي

.

لقد تمت دراسة الخواص التركيبيه بواسطه

مطياف حيود الشعه السينيه ودلت البنيه التركيبه علي انه مستطيلي متعامد

.

استخدمت معادله شيرر لحساب حجم البلوره ووجد انه يساوي

5.78

نانومتر

.

كما تمت دراسه الروابط

4

الكيميائيه بين ذرات المركبات بواسطه مطياف الشعه تحت الحمراء في المدي من

400

–

4000

سم

-

1

ووجد انهه تتمركز حول

.

616cm-1,1413cm-1,1663cm-1,2337cm

ّكذللك تمت دراسه الخواص الضوئيه بواسطه المطياف الضوئي للشعه فوق البنفسجيه وتم حساب فجوات

الطاقه للعينات

Cd

1-x

Sr

x

S

ذات التركيز

)

0.00,0.1,0.15,0.30,0.35x

(=

ووجد ت انها تساوي علي

التوالي

.

2.09eV

,2eV ,1.87eV ,1.79eV ,1.67eV

مما يعني

انها تنتمي الي ااشباه الموصلت