كلية العلوم
Permanent URI for this communityhttps://repository.neelain.edu.sd/handle/123456789/482
Browse
45 results
Search Results
Item The Influence of Cu on the Dielectric Properties of NiZnFe 2 O 4 Synthesized by Solid State Reaction Method(Al-Neelain University, 2020-12) Suzy Yahia Shareef AliAbstract In this research, Copper Ferrite, Zinc Ferrite, and Nickel Ferrite were prepared from oxides of Ni, Cu, Zn, and Fe using traditional ceramic method, X-ray diffraction data were collected and the formation of the spinal phase structure was found. The lattice parameter was foun to be 8.441 Afor ZnFe 2 O 4 835 A for NiF 2 O 4 n 8.34 9 A 8 or or CuF 2 O 4 . The Ni 0.6 Zn 0.4 Fe 2 O 4 ferrite was sintered at three different temperatures; namely 1100 ° C, 1200 ° C, and 1300 ° C and similar temperature control was applied to Cu 0.2 Ni 0.4 Zn 0.4 Fe 2 O 4 ferrite group. The energy band gap was calculated for Ni 0.6 Zn 0.4 Fe 2 O 4 and Cu 0.2 Ni 0.4 Zn 0.4 Fe 2 O 4 and was found to be 3.657 eV and 4.869 eV, respectively. The dielectric constant was investigated over a wide range using impedance spectroscopy and was found to decreases with the increase of frequency. Similar behavior was observed with the sintering temperature. In the same manner, the electric conductivity was found to decreases with the increase of frequency and sintering temperature as well. On the other hand, the electric resistivity was found to increases with both frequency and the sintering temperature. خلاصة في هذا البحث ، تم تحضير النحاس الفريت ، والزنك الفريت ، والنيكل الفريت من أكاسيد النيكل والنحاس والزنك والحديد باستخدام طريقة السيراميك التقليدية ، تم جمع بيانات حيود الأشعة السينية و تم العثور على تشكيل هيكل المرحلة الشوكية. تم foun المعلمة شعرية ZnFe 2 O 4 8 أو NiF 2 O 4 n 8 9 8 أو أو CuF 2 O 4. تم تلبيد Ni 0.6 Zn 0.4 Fe 2 O 4 فيريت عند ثلاثة درجات حرارة مختلفة وهي 1100 درجة مئوية ، 1200 درجة مئوية ، 1300 درجة مئوية وتم تطبيق تحكم مماثل في درجة الحرارة إلى Cu 0.2 Ni 0.4 Zn 0.4 Fe 2 O 4 مجموعة الفريت. تم حساب فجوة نطاق الطاقة لـ Ni 0.6 Zn 0.4 Fe 2 O 4 و Cu 0.2 Ni 0.4 Zn 0.4 Fe 2 O 4 ووجد أنه 3.657 فولت و 4.869 فولت على التوالي. ثابت العزل على نطاق واسع باستخدام التحليل الطيفي للمقاومة ووجد أنه يتناقص مع زيادة التردد. ولوحظ سلوك مماثل مع درجة حرارة التلبيد. في نفس بطريقة الطريقة ، تم العثور على الموصلية الكهربائية تتناقص مع زيادة التردد والتلبيد درجة الحرارة كذلك. من ناحية أخرى ، وجد أن المقاومة الكهربائية تزداد مع كليهما التردد ودرجة حرارة التلبيد.Item Determination Optical properties of Barium Titanium Oxide (Ba Ti O3) and its Applications in Solar Cells(Neelain University, 2019-12) Mohammed Alamin Aidroos BabekerAbstract The objectives of this Study is to prepare and study the optical properties of Nano material Barium titanium Oxide (Ba Ti O3) and applying it to use in photovoltaic applications (solar cells) by three different dye (Coumarin 500, Rhodamin B and Nile blue) to fabrication the solar cells performance. In this study determine the optical band gaps for three different dye (Coumarin 500, Rhodamin B and Nile blue), FTIR for Barium titanium Oxide (Ba Ti O3). And in this study calculating the efficiency of dye-sensitized solar cell by (I-V) characteristic for different dye, and find that efficiency increase when optical band gaps decrease. The study was recommended to upgrade the efficiency of solar cells. المستخلص هدفت هذه الدراسة لدراسة الخصائص البصرية لتيتانيوم الباريوم أوكسايد النانوني واستخدامه في التطبيقات الضوئية ( الخلايا الشمسية ) بعدد ثلاثة أصباغ. حُسبت فجوة الطاقة الضوئية للصبغات المستخدمة درست التحليل الكمي الطيفي لمادة تيتانيوم الباريوم أوكسايد، كما تمت دراسة كفاءة الخلايا الشمسية للعينات عن طريق المنحنى المميز (I-V) لمجموعة الأصباغ المختلفة التي تم استخدامها، ووجد أّن كفاءة الخلايا الشمسية تزيد بنقصان فجوة الطاقة الضوئية وأوصت الدراسة بتحسين كفاءة الخلايا الشمسية.Item The effect of annealing Temperatures on the Structural and the Optical Properties of Cobalt Oxide (Co3O4) Nano-particles(Neelain University, 2019-07) Bakhet Eltayeb Mosa MohamedAbstract In this study, Co3O4nano-particle was synthesized through hydrothermal method using cobalt nitrate hex hydrate Co(NO3)2.6H2O , ammonia hydroxide NH4OH and potassium hydroxide KOH. X-ray diffraction , Fourier transforms infrared spectroscopy and UV vis light spectroscopy at different annealing temperature of sample , effect of different annealing temperature on the particle size and on the structure and optical properties of cobalt oxide Co3O4nano-particle has been investigated .Single phase Co3O4nano-particles their structure was confirmed through X-ray diffraction analysis.All diffraction lines can be indexed to a cubic phase (Fd3m), as the annealing temperature increases, the density value of Co3O4is decrease, average crystallite sizes of the nano-particles as determined from the X-ray diffraction were found in the range of 21.2 to 30.1nm.The FTIR spectra can be seen by the bands at characteristic peak the positions 584.9-670.87cm-1 can be assigned to Co-O vibrations of their fig (4.4,4.6,4.7) was assigned to cobalt oxide but the bands at 3000-4000 cm-1 which can be assigned to the presence of water molecules, thus confirming that both O-H groups and water molecules are present in the cobalt oxide.The optical properties of cobalt oxide NPs we calculate by UV spectroscopy, shows the absorption peak is 275.665 nm and the absorption decreases with increasing annealing temperature and the optical absorption band gaps of the 𝐶𝑜3𝑂4 NPs were studied by UV–vis spectroscopy and were estimated is equal (3.569 ev, 3.620 ev, 3.665 ev, 3.727 ev) and we show while increasing temperature the band gap is increasing. The study recommended to study the magnetic properties of cobalt oxide, as well as the work of deformation with another material to improve the work of cobalt oxide, especially in lithium batteries and optical, electrical and magnetic properties. المستخلص في هذه الدراسة تم تحضير عينات من أكسيد الكوبالت النانوية وذلك بإستخدام طريقة التسخين الحراري العالي ، أخذت عينات من كوبالت نيترايتهايدروكسيد المائيةوتم حلها في 100 مل من الماء المقطر وهايدروكسيد الامونيا وهيدروكسيد البوتاسيوم. أستخدم كل من مطياف الاشعة السينية و مطياف التحليل الكمي للأشعة تحت الحمراء ومطايفية الأشعة فوق البنفسجية والمرئية لدراسة الخواص التركيبية والخواص الضوئية لأكسيد الكوبالت. حيث وجد أن كل العينات ذات درجات الحرارة المختلفة في المجموعة ذات وجه مكعب (Fd-3m)، وجد أنه عند زيادة التسخين تقل الكثافة للجزيئات وحُسب ثابت الشبيكة لكل العينات ويساوي 8.0650 Å, 8.0821 Å, 8.0650 Å, and 8.1773 Å، وأن متوسط المسافة بين ذرات المادة كانت في المدي (21.2 الي 30.1نانوميتر) وأن المسافة بين الذرات المادة تزيد عند زيادة درجة الحرارة. ظهرت زمرة Co-O عند الطول الموجي ما بين 584.9 الي 670.87 سم -1والإهتزاز الأساسي عند الرقم الموجي في المدي 38 وذلك للزمرة .O-Hأما إمتصاص العينة كان عند الرقم الموجي 275.66 نانو ميتر وأن الأمتصاصية تقل عند زيادة تسخين العينات. وجدت أن فجوة الطاقة الضوئية للعينة ذات درجة الحرارة 700 تساوى 3.727 الكترون فولت وللعينة 600 تساوي 3.66 الكترون فولت وللعينة 500 تساوي 3.62 الكترون فولت وأخيراً للعينة 400 تساوي 3.569 الكترون فولت ملاحظ أنه عند زيادة التسخين تزيد فجوة الطاقة الضوئية.أوصت الدراسة بدراسة الخصائص المغنطيسية لأكسيد الكوبالت ، وكذالك عمل تشويب مع مادة أخري لتحسين عمل أكسيد الكوبالت خصوصاُ في بطاريات الليثيوم والخصائص الضوئية والكهربية والمغنطيسية.Item Synthesis and Characterizations of Cu2NixZn1-xSnS4 for Solar Cells Applications (x = 0.0, 0.1, 0.2, 0.3, and 0.4)(جامعة النيلين, 2019-04) Eissa Abdelmjeed Moustafa SharafAbstract In This work synthesized Cu2NixZn1-xSnS4 samples and studied structural and optical properties and calculated efficiency of the cells. The Cu2NixZn1-xSnS4 samples, when (x = 0.0, 0.1, 0.2, 0.3and 0.4) were synthesized using hydrothermal method at 100C° for 4 hrs. Synthesized, structured and optical properties were studied in details using Fourier Transform Infrared spectroscopy (FT-IR) and Ultraviolet Visible Spectroscopy(UV-visible).FT-IR spectroscopy confirmed of spinal solar cells showing the absorption band around 662 cm-1, 1115 cm-1, 1641 cm-1, 2352 cm-1, 2924 cm-1 ,and 3260 cm-1. Absorption was found to be 0.0910 (a.u), 0.0898 (a.u), 0.0790 (a.u), 0.0677 (a.u) and 0.0609 (a.u) at the same wavelength 427.331 nm, and the absorption coefficient was found to be 420.527 %, 415.689 %, 368.768 %, 321.023 % and 290.322 % at the same wavelength 472.067 nm. The optical band gap energy were calculated using UV-Vis Spectroscopy, they were found to be 2.600 eV, 2.612 eV, 2.625 eV, 2.648 eV, and 2.664 eV which are semiconductor. The I-V curve was used to calculate the efficiency cells. The efficiency obtained from the cells were 0.142 %, 0.134 % , 0.126 % , 0.113 % and 0.1003 %, respectively. The energy band gap increased with the increasing of Ni concentration and the efficiency of cells were decreasing, due to the nickel effectiveness. In the future work, we recommend to use other chemical elements, with various methods, to study temperature effect and use of XRD technique. المستخلص يهدف هذا العمل إلي تحضير العينات ودراسة الخصائص التركيبية والضوئية وحساب كفاءة الخلايا الشمسية المصنعة. تم تحضير العينات ذات الصيغة الكيميائية Cu2NixZn1-xSnS4 حيث x = 0,0 , 0,1 , 0,2 , 0,3 و 0,4 باستخدام الطريقة الحرارية المائية في درجة حرارة 100 درجة مئوية خلال 4 ساعات. و ركزت الدراسة على تحضير الخواص التركيبية و الخواص الضوئية للعينات . باستخدام مطيافية الأشعة تحت الحمراء, مطياف الأشعة فوق البنفسجية و الضوء المرئي. و تم التحق من الروابط الكيميائية للمركبات بواسطة مطياف الأشعة تحت الحمراء و وجدت أنها تتمركز حول 662 سم-1 , 1115 سم-1 , 1641 سم-1 , 2352 سم-1 و 2924 سم-1. ووجد أن الامتصاصية نقصت من 0,0910 إلى 0,0609 لتر/ مول.سم عند الطول الموحي 427.331 نانومتر أما معامل الامتصاص أيضا نقصت من 420.527 % إلى 290.322 % عند الطول الموحى 472.067 نانومتر . كما تم حساب فجوات الطاقة من بيانات مطياف الأشعة فوق البنفسجية و الضوء المرئي ووجدت أنها 2.600 , 2.612 , 2.625 , 2.648 و 2.664 إلكترون.فولت مما يعني أنها أشباه موصلات. كما تم استخدام منحنى (الجهد– التيار) للخلايا الشمسية لقياس كفاءة الخلايا. وكانت الكفاءة في الخلية المصنعة هي 0,14 % , 0,13 %, 0,126 %,0,113 % و3 0,100 % بالترتيب. ووجد أن كلما زاد تركيز النيكل تزيد فجوة الطاقة و تقل كفاءة الخلية و هذا يدل على أثر النيكل في المركب. في الدراسة المستقبلية أوصي باستخدام عناصر كيميائية أخرى , طرق تضير أخرى , دراسة تأثير درجة الحرارة و استخدام جهاز الأشعة السينية.Item Quzmtizalion Of The Grzivitmional Field ln Very Early Universe(Neelain University, 2005) Awud Alsikh Hamed(Einstein fiellf equation of genel'a[ refiztiuity succeeded in zfeserifiing a numfier of gravitationaf p/ienomena in agreement wit/Z astr0pfi_ysica[measurements. 'Unfortullatel:y, it is sufler from fieing isoQ1tezffi'o1n tfie otfzer Erancfies of p/zysics fiecause tfie fiiw of tfze conservation of energy and momentum is not satilsfiezi jllso t/ie cosmofogicaf appfication of QR gives many profifiznzs wfiicfi neeef solution, so generafizezffiefif equation usezf for tfizlspuqzose. - In tfiis t/zesis s0[ution of some pro5[ems are introcfuce namefy quantization qfgrwuitationaf waves, quantization of radiatiozz, matter amt" inflation eras. {Non-[inenr equation 'wi[[ /iefpfitffy wgpfilin tfie quantization during inffiltion, razfiation, and matter eras.Item Synthesis and Characterization of (Ba (1-x) Mg x Ti (1-x) Mn x O3) Single Preovskite Oxide(2018) Mohammed Awadh Saeed Al-AmeriABSTRACT Five samples of single perovskite oxides of formula Ba(1-x) Mg x Ti(1-x) Mn xO3 where x = 0.01, 0.2, 0.03, 0.04, and 0.05 were synthesized using solid state reaction method, and the samples were calcinated at . All samples were investigated by spectroscopy techniques such as, X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and Ultraviolet Visible Spectroscopy (UV-visible), and. The XRD results confirmed that the five samples had a cubic phase, and the average of lattice constants, and the average of grain sizes increased with dopant from sample 1 to sample 4 ( , , , and ), (29.3nm, 32.4nm,36.15 nm , and 37.98 nm) respectively, and they decreased with contents of Mg and Mn in sample 5 ( ) , (37.5 nm) respectively .Also the intensity increased with dopant of Mg and Mn in samples1,2,3,and 5 , and it decreased in sample 4 . The FTIR spectroscopy results showed that the transmittance of the five samples decreased with contents of Mg and Mn at . On other hand, the Ultraviolet Visible Spectroscopy (UV) proved that the absorption of five samples have been increased with increasing of Mg and Mn doping in , and the optical band gap energy increased with Mg and Mn contents at (3.18, 4.31, 4.35, 4.39, and 4.43 eV), which results in decreasing of reflective indexes (2.31, 2.10, 2.09,2,089, and 2.083) respectively . These results were attributed to the doping of elements in A and B sites . المستخلص تم تحضير عينات من أكاسيد البروفسكايت الأحادية Ba(1-x) Mg x Ti(1-x) Mn xO3 حيث أن (x = 0.01, 0.02, 0.03, 0.04, and 0.05) وتمت معالجتها حراريا باستخدام الطريقة التقليدية وهي تفاعل الحالة الصلبة وحيث أن جميع العينات تم تكليسها عند 1200 درجة مئوية. جميع العينات تم تحليلها بواسطة تقنيات الطيف المختلفة مثل مطياف حيود الأشعة السينية و مطياف الأشعة تحت الحمراء و المطياف الضوئي للأشعة فوق البنفسجية. تم التأكد بواسطة مطياف حيود الأشعة أكد أن جميع العينات لها طور كيميائي مكعب و أن ثابت الشبيكة وحجم الحبيبات تزداد من العينة الأولى إلى العينة الرابعة (4.0512,4.2086 , 5.0087 , 5.1955 بوحدات الأنجستروم) و (29.3, 32,4 ,36.15, 37.98 بوحدات النانومتر) على الترتيب وكما أن ثابت الشبيكة وحجم الحبيبات تقل عند العينة الخامسة ( ), (37.5نانومتر) على الترتيب . كما أن جهاز قياس طيف الأشعة تحت الحمراء أثبت أن النفاذية تقل بزيادة نسبة تشويب عنصري المغنيسيوم والمنجنيز في مركب تيتاتات الباريوم .ومن ناحية أخرى المطياف الضوئي للأشعة فوق البنفسجية أكد أن الامتصاصية للخمس العينات تزداد بزيادة نسب التشويب لعنصري المغنيسيوم والمنجنيز , وتم حساب فجوة الطاقة ووجدت أنها تزداد بزيادة نسبة التشويب (3.18, 4.31 ، 4.35، 4.39، 4.43 بوحدات الإلكترون فولت ) على الترتيب . وكذلك فإن معامل الانكسار يقل بزيادة نسبة التشويب للعنصرين المذكورين أعلاه (2.31 ,2.10 , 2.09 , 2.089, 2.083 ) . جميع النتائج تعود إلى تشويب عنصري المغنيسيوم والمنجنيز في تيتاتات الباريوم .Item Synthesis and antibacterial Applications of CuO nanostructures(2018) Mustafa Qais shehabAbstract In this work nano copper oxide were prepared using hydrothermal method. Thin films were prepared on glass substrates by drop casting methods All prepared samples were studied with different apparatus and techniques, the X-ray diffraction patterns for all samples show polycrystalline structure for CuO, crystallite size and structural parameters were calculated from x-ray patterns. EDX test was performed and all samples confirm pure products of CuO where peaks for Cu and O appears no impurities peaks found. Scanning electron microscopy images for (0.02 M) show nanoparticles of CuO with grain size ranging between (40-100 nm). While for (0.04 M) nano rods were appeared with diameters between (100-500 nm) and (0.06 M) images looks like micro permed with nano layers. The optical properties test decreasing in transmission with increasing molarity and decreasing of energy gap with increasing the molarity. All the samples show high results for inhibition bacteria activity in the rate of (99 %) and indicate that CuO nano structure is promising as antibacterial agent. الـخــلاصــــة في هذا العمل , تم تحضير اوكسيد النحاس النانوية بطريقة الهايدروثيرمال. تمت دراسة خصائصها العينات المحضرة باستخدام تقنيات مختلفة, اظهرت قياسات حيود الاشعة السينية لاوكسيد النحاس ذات تركيب متعدد التبلور. مقاس البلورة والعوامل التركيبية تم حسابها لجميع العينات. لم يلاحظ اي قمم لشوائب اخرى في نموذج حيود الاشعة السينية لجميع العينات. واظهرت قياسات تشتت طاقة الاشعة السينية ان جميع العينات قمة عالية جداً للنحاس وقمة صغيرة للاوكسجين والتي تشير الى أوكسيد النحاس النانوية مع عدم ظهور قمم اخرى اي كشوائب نتيجة عملية التحضير . اظهرت نتائج صور المجهر الالكتروني الماسح من اوكسيد النحاس تراكيب نانوية مختلفة حيث عند المولارية (0.02 مول) جسيمات نانوية تتراوح قياساتها بين (40-100 نانو متر) بينما عند المولارية (0.04 مول) ظهرت لنا قضبان نانوية ذات اقطار مختلفة تتراوح بين (50-500 نانو متر) وعند المولارية (0.06 مول) ظهرت تراكيب مايكروية على شكل اهرامات ذات طبقات بسمك نانوي . واظهرت القياسات البصرية لأوكسيد النحاس النانوية انخفاض النفاذية مع زيادة المولارية. اوكسيد النحاس النانوية واظهرت تغير في فجوة الطاقة (انخفاض فجوة لطاقة مع زيادة المولارية ) . كما تم اجراء فحص فعالية جسيمات اوكسيد النحاس النانوية ضد بكتيريا (Staphylococcus aureus , Esherichia coli ) ودورها في تقليل نشاطها وتثبيطها لكافة العينات المحضرة بمولاريات مختلفة واظهرت النتائج نسبة قتل تصل الى (99%).Item Cu Doped ZnO as Transparent Electrode for Dye Sensitized Solar Cell )DSSC((2017) Khamael Ibrahim AbdulwahidAbstract Pure and Cu doped ZnO nanoparticles, with different doping ratio (0, 2, 4, 6 and 8) at%, were prepared by hydro thermal method at 90 ᵒC from zinc nitrate Zn(NO3)H2O and sodium hydroxide NaOH as precursors, and with substitution additive of CuO as a dopant at the selected ratio. The effect of Cu doping ratio on structural and optical properties for synthesized nanoparticles were studied by X-ray diffraction, UV-visible absorbance and Fourier transform infrared spectroscopy to find the optimum conditions for use the produced nanoparticles with iodine dye in solar cell application X-ray diffraction measurements show polycrystalline structure for all samples identical with ZnO standard peaks. The crystallinety decrease with increasing doping ratio. The non-uniform strain (ε), calculated by Williamson-Hall (W-H) plot shows that the ε increase with increasing Cu ratio specially at 8%. The maximum value for crystalline size at 2% Cu then decreases with increasing doping ratio. Optical properties showed that the transmittance increases with increasing doping ratio to 8% reaching values higher than 90% in the visible region. The energy gap was direct transition, and increasing of Cu content from 0 to 2% leads to decrease the optical band gap from 3.20 to 3.14 eV and then increase to 3.26 eV at 8% Cu due to decreasing the nanosize. FTIR patterns show small peaks located in the range from 420 to 620 cm-1 corresponding to Zn-O vibrations, indicate on ZnO formation. The I-V characteristics for DSSC under illumination , for samples based on Cu doped ZnO NPs with different ratio, show that the efficiency increase with increasing the Cu dopant ratio to reach 0.0439 at 8% Cu content. الخلاصة تم تحضير جسيمات اوكسيد الخارصين النانوية النقية والمشوبة بالنحاس وبنسب ذرية مختلفة (0 و 2 و 4 و 6 و 8) ٪ بالطريقة الحرارية المائية عندᵒC 90 من نترات الزنك (ZnNO3) H2O وهيدروكسيد الصوديوم NaOH كمواد اولية، مع اضافة تعويضية من CuO وبالنسب المحددة. تم دراسة تأثير نسبة التشويب بالنحاس على الخصائص الهيكلية والبصرية للجسيمات النانوية المحضرة، بواسطة حيود الأشعة السينية وامتصاص الأشعة فوق البنفسجية المرئية وتحويل فورييه للتحليل الطيفي للأشعة تحت الحمراء للعثور على الظروف المثلى لاستخدام جزيئات النانو المنتجة مع صبغة اليود في تطبيقات الخلايا الشمسية أظهرت قياسات حيود الأشعة السينية تركيب متعدد التبلور لجميع العينات متطابقة مع قمم القياسية لأوكسيد الزنك. و انخفاض درجة التبلور مع زيادة نسبة التشويب. الاجهاد الغير منتظم في الشبيكة (ε)، و المحسوب باستخدام معادلة ويليامسون-هول يدل على زيادة ε مع زيادة نسبة النحاس خاصة في 8٪. بينما كانت اكبر قيمة للحجم البلوري عند النحاس 2٪ ثم تنخفض مع زيادة نسبة التشويب. أظهرت الخصائص البصرية أن النفاذية تزداد مع زيادة نسبة التشويب إلى 8٪ تصل إلى قيم أعلى من 90٪ في المنطقة المرئية. وكانت فجوة الطاقة ذات انتقال مباشر، وزيادة محتوى النحاس من 0 إلى 2٪ يؤدي إلى تقليل فجوة الطاقة البصرية من 3.20 إلى 3.14 فولت ومن ثم زيادة إلى 3.26 فولت عند 8٪ النحاس بسبب انخفاض الحجم النانوي. بينت منحنيات FTIR قمم صغيرة تقع في نطاق 420-620 سم -1 المقابلـــة للاهتزازات Zn-O، و التي تدل على تشكيل أكسيد الزنك. بينت خصائص I-V لخلايا الصبغة DSSC تحت الإضاءة، للعينات المحضرة باستخدام عينات ZnO المشوب بالنحاس مع نسب مختلفة، يدل على زيادة الكفاءة مع زيادة نسبة التشويب تصل إلى %0.0439 عند محتوى النحاس 8٪Item Optimization of Radiation Dose in Pediatric Computed Tomography(2010) Nawar Ahmed EL Hussein AL Hajالخلاصة بالرغم من مخاطر التصوير الطبقي التشخيصي للأطفال نتيجة تعرضهم لجرعة اشعاع عالية ، الا انها تعتبر أداة لحفظ الحياة ولا تزال هناك فائدة كبيرة ترجى منه. تعتبر الموازنة بين الخطر والفائدة قضية صحة عامة . هذه الأطروحة تهدف الي: (i). قياس الجرعة الاشعاعية ،(ii).أستنتاج الجرعة الفعالة للأطفال و(iii). أمثلة الجرعة الأشعاعية أثناء التصوير الطبقي للأطفال . تم قياس الجرعة الاشعاعية خلال اربعة اشهر لعدد 38 طفل من كل من: (i). مركز النيلين الطبي (ii).المركز المتطورو (iii). مستشفى الرباط الوطني. أجهزة الأشعة المقطعية المقطعية المستخدمة هنا هي أجهزة حلزونية تعطي قيم الجرعة الاشعاعية بوحدات (CTDIvol)و (DLP).بعد خضوعها للمعايرة من قبل هيئة الطاقة الذرية السودانية. تم تقسيم المرضى من حيث نوع الأختبار المجري كالأتي: 29لتصوير الرأس، 4 لتصوير الصدر و4 لتصوير البطن كالاتى متوسط الجرعات المقاسة كالاتي: متوسط الجرعة لوحدة الطول 240.12±111 ملي قري في السم، مؤشر الجرعة الحجمي 16.68± 6.9 قري ومتوسط الجرعة لوحدة الطول 239.7 ± 244.9 ملي قري في السم و مؤشر الجرعة الحجمي 16.28 ± 12.9 في كل من مستشفي الرباط الجامعي ومركز النيلين التشخيصي علي الترتيب أظهرت هذه الاطروحة تباين في عوامل التعريض في المراكز الثلاث بالنسبة للجرعة الاشعاعية، مؤشر الكتلة وكذلك في عوامل التصوير (mAs - kVp) والتي تعطي نمو مختلف في عوامل الجرعة الفعالة. من العوامل غير الموضوعة في الحسبان العمر وهذه يعرض الاطفال لجرعة اشعاعية عالية غير ضرورية أثناء التصوير الطبقي.Item MEASURMENTS OF RF/MW RADIATION EMITTED FROM SELECTED MOBILE-PHONE BASE- STATIONS IN SUDAN(2008) Abdelfatah Mohamed Mohamed Ahmed Ahmed